硅烷交联POE／PE-LLD软管材料的制备

宋小辉;毕婷婷;王仁杰;李林;陈金周;牛明军

【期刊名称】《工程塑料应用》 【年(卷),期】2014(000)010

【摘 要】The silane cross-linked POE/PE–LLD hose material was developed on single screw extruder by means of two-steps silane cross-linking and reaction extruding principle. The effects of POE content,silane coupling agent kinds,DCP contents and cross-linking time on the gel content and tensile strength of silane cross-linked POE/PE–LLD hose material were discussed. The modified POE/PE–LLD hose material with excellent integrated function was obtained. The results indicate that when POE/PE–LLD=50/50,the dosage of A151 is 3%,DCP is 0.05%and DBTDL is

0.5%,cross-linking time is 12 h,the gel rate is 69.4%, the tensile strength is up to 22.8 MPa. Moreover,retention of tensile strength is 94% after the aging processing. The material can be used for cross-linked POE/PE–LLD hose,which can withstand high temperature and age.%通过硅烷交联两步法，利用反应挤出原理在单螺杆挤出机上进行硅烷交联乙烯–辛烯共聚物(POE)／线型低密度PE (PE–LLD)软管材料的制备；重点考察了POE用量、硅烷偶联剂种类、引发剂用量及交联时间等对POE／PE–LLD凝胶率、拉伸强度的影响，制得了性能优良的软管材料。研究表明，当POE／PE–LLD质量比为50／50，硅烷偶联剂A151、引发剂过氧化二异丙苯、催化剂二月桂酸二丁基锡用量分别为3%，0.05%，0.5%，交联时间为12 h时，材料的凝胶率达69.4%，拉伸强度达22.8

MPa，耐老化处理后材料的拉伸强度保持率为94%，可应用于耐高温、耐老化软管的生产。

【总页数】5页(P28-32)

【作 者】宋小辉;毕婷婷;王仁杰;李林;陈金周;牛明军

【作者单位】郑州大学材料科学与工程学院，郑州 450001;郑州大学材料科学与工程学院，郑州 450001;郑州大学材料科学与工程学院，郑州 450001;郑州大学材料科学与工程学院，郑州 450001;郑州大学材料科学与工程学院，郑州 450001;郑州大学材料科学与工程学院，郑州 450001 【正文语种】中 文 【中图分类】TQ325.1 【相关文献】

1.无卤阻燃硅烷交联POE复合材料的制备及性能研究 [J], 徐伟;金晓旦;段景宽;汪根林;江平开

2.POE的交联过程及制备方法对发泡材料结构的影响 [J], 孙小杰;梁文斌 3.硅烷交联无卤阻燃PP/POE复合材料的制备和性能 [J], 张建耀 4.氧化镧对硅烷交联PE-LLD热性能的影响 [J], 李红山;张艺;许家瑞

5.聚丙烯种类对硅烷交联PP/POE(EPDM)共混材料性能的影响 [J], 张忠州;王磊;路敏;蒋成;彭辉;牛明军

因版权原因，仅展示原文概要，查看原文内容请购买